고 코발트 - 니켈 이차 경화강에서의 M2C 석출물의 성장 거동에 관한 연구 - Part 1 . 시효처리의 영향A Study on the Growth Behavior of M2C Precipitates in the High Co-Ni Secondary Hardening Steel-Part I. Effect of Tempering Treatments

Cited 0 time in webofscience Cited 0 time in scopus
  • Hit : 481
  • Download : 0
The effect of tempering on the growth behavior of M₂C precipitates was examined. Applied tempering temperatures were 468, 482 and 510℃, and tempering time varied from 1 to 400 hours. The value of peak hardness was HRc 55 in all temperatures and the shift of peak hardness to earlier tempering time occurred with an increase in temperature. The peak hardness was obtained, when the average length and diameter of M₂C carbides were 4∼8 ㎚ and 1.5∼2.5 ㎚, respectively. The size of M₂C carbides increased with tempering time, and the size of carbides at 510℃ was larger than that at 482 or 468℃ in all tempering time. The aspect ratio of M₂C carbides was almost 3 in all tempering conditions. The amount of precipitated austenites increased with tempering time and temperatures. Experimental studies of grow th behavior of the carbides in this steel have been made by using TEM, SEM and X-ray diffraction.
Publisher
Korean Institute of Metals and Materials
Issue Date
1995-10
Language
Korean
Citation

JOURNAL OF KOREAN INSTITUTE OF METALS AND MATERIALS, v.33, no.10, pp.1330 - 1336

URI
http://hdl.handle.net/10203/73210
Appears in Collection
MS-Journal Papers(저널논문)
Files in This Item
There are no files associated with this item.

qr_code

  • mendeley

    citeulike


rss_1.0 rss_2.0 atom_1.0