YAG : Ce phosphor particles prepared by ultrasonic spray pyrolysis

Cited 228 time in webofscience Cited 0 time in scopus
  • Hit : 809
  • Download : 104
Spray pyrolysis was applied to the preparation of fine YAC:Ce phosphor particles. The characteristics of particles such as crystallinity, morphology, and photoluminescence were investigated. Phase-pure YAC:Ce particles with high crystallinity were obtained after annealing at lower temperatures than those of conventional preparation processes. The mean size of the particles increased from 0.46 to 1.2 mu m when the overall solution concentrations were changed from 0.03 to 1 mol/L, The YAG:Ce particles annealed at 1300 degrees C were nonaggregated and spherical. The particles absorbed excitation energy in the range 403-510 nm, and the maximum excitation wavelength was near 470 nm. The YAG:Ce particles showed broad emission peaks in the range 480-650 nm and had maximum intensity at 528 nm. The photoluminescence intensity of the particles increased monotonically with increasing annealing temperature and showed the maximum value at 1 at% Ce, (C) 2000 Elsevier Science Ltd. All rights reserved.
Publisher
PERGAMON-ELSEVIER SCIENCE LTD
Issue Date
2000-03
Language
English
Article Type
Article
Keywords

BRIGHT GREEN PHOSPHOR; LUMINESCENCE; TB

Citation

MATERIALS RESEARCH BULLETIN, v.35, no.5, pp.789 - 798

ISSN
0025-5408
URI
http://hdl.handle.net/10203/9218
Appears in Collection
CBE-Journal Papers(저널논문)
Files in This Item
This item is cited by other documents in WoS
⊙ Detail Information in WoSⓡ Click to see webofscience_button
⊙ Cited 228 items in WoS Click to see citing articles in records_button

qr_code

  • mendeley

    citeulike


rss_1.0 rss_2.0 atom_1.0