Synthesis of zeolites from halloysite : active species to form zeolites = 고령토로부터 제올라이트의 합성과 합성반응에 관여하는 활성 화학종에 관한 연구active species to form zeolites

Cited 0 time in webofscience Cited 0 time in scopus
  • Hit : 430
  • Download : 0
In this study a halloysite which is one of the kaolin group minerals was used as sources of alumina and silica in the synthesis of several zeolites. The reactivity of alumina was determined by chemical dissolution method. The reactivity of alumina was varied upon calcination temperature. The reactivity of silica showed no discernible change in the range of 550 to 1050℃. IR spectra of halloysites indicated that $AlO_4$ peak near $800cm^{-1}$ became intense in the range of 550 to 850℃ and reduced at higher temperature. IR spectra of acid leached halloysite indicated that $AlO_4$ peak reduced in the range of 550 to 850℃ and that at higher temperatures the spectra showed no change. The results suggested that the acid leachable alumina in halloysite is a reactive species for the formation of zeolite and that the alumina is tetrahedrally coordinated. The effective $SiO_2/Al_2O_3$ mole ratio of halloysite to be transformed into zeolites could be determined by chemical dissolution method and the ratio could be controlled by calcining temperature followed by adding reactive alumina compound and/or by mixing the low temperature calcined halloysite and high temperature calcined halloysite. The faujasite type zeolities and the attrition resistant zeolite 4A could be easily synthesized from halloysite with controlling the effective $SiO_2/Al_2O_3$ mole ratio.
Advisors
Uh, Young-Sun어용선
Description
한국과학기술원 : 화학과,
Publisher
한국과학기술원
Issue Date
1985
Identifier
64380/325007 / 000831528
Language
eng
Description

학위논문(석사) - 한국과학기술원 : 화학과, 1985.2, [ [vi], 42 p. ]

URI
http://hdl.handle.net/10203/32414
Link
http://library.kaist.ac.kr/search/detail/view.do?bibCtrlNo=64380&flag=dissertation
Appears in Collection
CH-Theses_Master(석사논문)
Files in This Item
There are no files associated with this item.

qr_code

  • mendeley

    citeulike


rss_1.0 rss_2.0 atom_1.0