Wear behavior and microstructural characterization of translucent multilayer zirconia

Cited 0 time in webofscience Cited 0 time in scopus
  • Hit : 151
  • Download : 0
Objective. To characterize the composition, microstructure and wear properties of a multi layer translucent zirconia relative to the conventional 3Y-TZP. Methods. Two types of ceramics were evaluated: a multilayer zirconia (MULTI, IPS e.max ZirCAD Multi, Ivoclar Vivadent) and a control 3Y-TZP (IPS e.max ZirCAD LT, Ivoclar Vivadent). Pre-sintered CAD-CAM blocks were cut, ground, sintered and polished to 1 mu m finish. The phase fraction and grain size were measured using XRD and FE-SEM. For wear testing (n = 12), square-shaped specimens (16 x 16 x 1 mm) were adhesively bonded to a dentin analog. Sliding wear tests were performed using a spherical zirconia antagonist (r = 3.15 mm), with 30 N load at 1.5 Hz for 500,000 cycles in water. Optical and scanning electron microscopes and 3D laser scanner were used for quantitative wear analyses. Data were analyzed using Student's t-test (alpha = 0.05). Results. For MULTI, the enamel layer had the highest cubic content and the largest grain size, followed by the two transition layers, and the dentin layer. 3Y-TZP showed the smallest grain size and cubic content. A significant amount of wear was observed in both materials up to 50,000 cycles until it reached a plateau. MULTI showed higher volume loss and greater wear depth than 3Y-TZP (p < 0.01). The higher volume loss was associated with extensive lateral fracture, leading to material spalling from the surface of cubic-containing zirconias. Significance. The wear pattern in multi-layered zirconia was more severe than 3Y-TZP. Additionally, the different layers of the multi-layered zirconia had similar wear behavior.
Publisher
ELSEVIER SCI LTD
Issue Date
2020-11
Language
English
Article Type
Article
Citation

DENTAL MATERIALS, v.36, no.11, pp.1407 - 1417

ISSN
0109-5641
DOI
10.1016/j.dental.2020.08.015
URI
http://hdl.handle.net/10203/277760
Appears in Collection
MS-Journal Papers(저널논문)
Files in This Item
There are no files associated with this item.

qr_code

  • mendeley

    citeulike


rss_1.0 rss_2.0 atom_1.0