Low-cycle fatigue behaviors of two heats of SA508 Gr.1a low alloy steel in 310 degrees C air and deoxygenated water-Effects of dynamic strain aging and microstructures

Cited 13 time in webofscience Cited 0 time in scopus
  • Hit : 262
  • Download : 0
The low cycle fatigue (LCF) resistances of two heats of SA508 Gila low alloy steel, heat FP with a ferrite pearlite microstructure and heat BA with a bainite microstructure, were compared in 310 degrees C air and deoxygenated water. The LCF life of heat FP was shorter than that of heat BA in 310 degrees C deoxygenated water while the LCF life of both heats was comparable in 310 degrees C air. Such behaviors were explained considering the dynamic strain aging (DSA) behaviors in both environments and their microstructures. Based on cyclic stress and tensile behaviors, it was found that heat BA showed higher degree of DSA than heat FP in 310 degrees C air, but both showed similar degree of DSA in 310 degrees C deoxygenated water because the degree of DSA was reduced by absorbed hydrogen. In case Of microstructure. heat FP had a lower fatigue cracking resistance due to the stress concentration effect in ferrite pearlite interface. As a result, in 310 degrees C air, where the effect of DSA was large enough to override the microstructure effect. LCF life of heat BA was similar to that of heat FP. On the other hand, LCF life of heat BA was longer than that of heat FP in 310 degrees C deoxygenated water, where the effect of DSA was not so significant. (C) 2013 Elsevier By. All rights reserved.
Publisher
ELSEVIER SCIENCE SA
Issue Date
2013-09
Language
English
Article Type
Article
Keywords

AUSTENITIC STAINLESS-STEEL; PRESSURE-VESSEL STEELS; DUAL-PHASE STEEL; CRACK-GROWTH; CORROSION-FATIGUE; 310-DEGREES-C; DEFORMATION; HYDROGEN; FERRITE; MECHANISMS

Citation

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, v.580, pp.41 - 50

ISSN
0921-5093
DOI
10.1016/j.msea.2013.05.049
URI
http://hdl.handle.net/10203/192950
Appears in Collection
NE-Journal Papers(저널논문)
Files in This Item
There are no files associated with this item.
This item is cited by other documents in WoS
⊙ Detail Information in WoSⓡ Click to see webofscience_button
⊙ Cited 13 items in WoS Click to see citing articles in records_button

qr_code

  • mendeley

    citeulike


rss_1.0 rss_2.0 atom_1.0