Thick SmBCO/IBAD-MgO Coated Conductor for High Current Carrying Power Applications

Cited 9 time in webofscience Cited 0 time in scopus
  • Hit : 347
  • Download : 0
Long-length Sm(1+x)Ba(2-x)Cu(3)O(7-y) (SmBCO) coated conductor was fabricated using ion beam assisted deposition(IBAD)-MgO template (LaMnO(3)/IBAD - MgO/Y(2)O(3)/Al(2)O(3)/Hastelloy) by the reactive co-evaporation method for electric power applications. SmBCO superconducting layers with thicknesses from 1 to 3 mu m were deposited to investigate the effect of SmBCO thickness on the in-plane texture, surface morphology and superconducting properties. In this study, the optimal deposition conditions were examined to make thick SmBCO coated conductor without degradation of critical current density. The oxygen partial pressure and temperature were controlled in the range of 1 similar to 20 mTorr and 600 similar to 800 degrees C, respectively. SmBCO/IBAD-MgO coated conductors showed high critical current densities over 2.0 Ma/cm(2) with small amount of degradation by increasing the thickness of superconducting layer up to 3 mu m. The critical current of 637.5 A/cm-w (J(C) = 2.12 MA/cm(2)) at 77 K in self-field was obtained in 3 mu m-thick and 1 m long coated conductor. This is the highest critical current reported so far of the coated conductor with SmBCO superconducting layer deposited by co-evaporation.
Publisher
IEEE-INST ELECTRICAL ELECTRONICS ENGINEERS INC
Issue Date
2010-06
Language
English
Article Type
Article; Proceedings Paper
Keywords

CRITICAL-CURRENT DENSITY; COEVAPORATION; FILMS; FIELD

Citation

IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, v.20, pp.1545 - 1548

ISSN
1051-8223
URI
http://hdl.handle.net/10203/99681
Appears in Collection
PH-Journal Papers(저널논문)
Files in This Item
There are no files associated with this item.
This item is cited by other documents in WoS
⊙ Detail Information in WoSⓡ Click to see webofscience_button
⊙ Cited 9 items in WoS Click to see citing articles in records_button

qr_code

  • mendeley

    citeulike


rss_1.0 rss_2.0 atom_1.0