Synthesis of ordered mesoporous carbons using furfuryl alcohol and characteristics of various ordered mesoporous carbons after high temperature treatment = 퍼퍼릴 알코올을 이용한 메조구조규칙성 탄소의 합성과 다양한 메조구조규칙성 탄소의 고온 처리 후의 특성규명에 관한 연구

Cited 0 time in webofscience Cited 0 time in scopus
  • Hit : 414
  • Download : 0
Ordered mesoporous carbons (OMC) were synthesized using a furfuryl alcohol carbon precursor and a SBA-15 silica template under the ambient pressure conditions using template-directed synthesis strategy. Furfuryl alcohol was polymerized using Lewis acid, such as framework aluminum, $Co^{2+}, Ni^{2+}$, and $Fe^{3+}$ ions, and it was further carbonized by heating up to 900℃ inside of the SBA-15 template. The resulting OMC products were characterized by X-ray powder diffraction (XRD), nitrogen adsorption - desorption, transmission electron microscope (TEM), differential scanning calorimetry (DSC), $^1H$ NMR, and X-ray adsorption fine structure (XAFS) experiments. The correlation between the extent of the polymerization of furfuryl alcohol and the resulting mesopore structures were investigated with various conditions. Especially, if $Co^{2+}, Ni^{2+}$, and $Fe^{3+}$ ions were employed as Lewis acid catalysts for the polymerization of furfuryl alcohol, the final OMC products were supported with magnetic nanoparticles by the reduction of metal ions and could be attracted by strong hard magnets. Thus, the OMC products containing magnetic nanoparticles can be applied for the easy preparation of adsorbents for magnetic separations. The OMC products with 2-D hexagonal symmetry, obtained by SBA-15 templates with various pore diameters and by furfuryl alcohol or acenaphthene as a carbon source, were heated with various temperatures up to 2400℃. The structural changes of OMC structures after the high temperature heating were characterized by XRD, nitrogen adsorption -desorption, and TEM. The results show that the larger carbon-rod diameters exhibit the more endurance to the thermal destructions. The CMK-5 structures with tube-type framework structures from a furfuryl alcohol carbon source undergo the microphase transformations with rising temperatures, and finally the CMK-5 structures are converted to graphitic carbon framework, which are aligned with rod directions. A...
Ryoo, Ryongresearcher유룡researcher
한국과학기술원 : 화학과,
Issue Date
249486/325007  / 020005129

학위논문(박사) - 한국과학기술원 : 화학과, 2005.8, [ xii, 106 p. ]


High Temperature; Ordered Mesoporous Carbon; Furfuryl Alcohol; 고온 가열; 메조구조 규칙성 탄소; 퍼퍼릴 알콜

Appears in Collection
Files in This Item
There are no files associated with this item.


  • mendeley


rss_1.0 rss_2.0 atom_1.0